Epitaxial Barium Titanate (BaTiO3) thin films were fabricated on Platinised (Pt 111) Si/SiO 2 wafer by spin coating of metalloorganic sol gel solution. A preferred directional growth was obtained for BT (BaTiO3) thin film by employing Platinum (111) coating as a template. BT film was heat-treated at 700°C for 1 hour using the direct insertion method. The film was epitaxially grown with (111) and (211) being parallel to the Pt(111). The epitaxial growth of the thin film along (111) orientation was confirmed by XRD, AFM and SEM. The cross sectional view of SEM image showed that most nuclei were formed at the interface between the film and the substrate. BT thin film was characterized for its ferroelectric, dielectric and piezoelectric properties. Ferroelectric hysteresis measurement yielded high spontaneous polarization value (12.3µC/cm 2 ) comparatively at low electric field (150kV/cm). Substantial increase in piezoelectric d33 was explained in the light of domain wall engineering.