Heesup Choi; Masumi Inoue; Risa Sengoku; Hyeonggil Choi
Abstract
In this study, it is possible to disperse effectively cracked using synthetic fiber, an examination of the most suitable self-healing conditions was performed on the above crack width 0.1mm. As a result, effective crack dispersion using polyvinyl alcohol (PVA) fibers with polar OH - groups, as well as ...
Read More
In this study, it is possible to disperse effectively cracked using synthetic fiber, an examination of the most suitable self-healing conditions was performed on the above crack width 0.1mm. As a result, effective crack dispersion using polyvinyl alcohol (PVA) fibers with polar OH - groups, as well as improved self-healing for cracks that are larger than 0.1 mm in width, posing concerns of CO2 gas and Cl - penetration, were observed. Also, CO3 2- reacts with Ca 2+ in the concrete crack, resulting in the precipitation of a carbonate compound, CaCO3. Based on this, it is deemed possible for the recovery of effective water tightness and strength recovery through effective freezing-thawing resistance to be made from cracks that are larger than 0.1 mm in width. In addition, it was determined that, as for the most suitable self-healing conditions in the inside and surface of the cracks, calcium hydroxide (Ca(OH)2) solution with CO2 micro-bubble was more effective in promoting the self-healing capability than water with CO2 micro-bubble.
Deepak Patil; Ajay Vasudeo Rane; K Kanny; Abitha V K; Anagha Sabnis
Abstract
Novel self-repairing Urea-Phenol-Formaldehyde (UPF) microcapsules containing linseed oil were prepared via in-situ polymerization in an oil-in-water emulsion. The main purpose of encapsulation is to control the release of linseed oil, when external conditions such as mechanical stress or energy cause ...
Read More
Novel self-repairing Urea-Phenol-Formaldehyde (UPF) microcapsules containing linseed oil were prepared via in-situ polymerization in an oil-in-water emulsion. The main purpose of encapsulation is to control the release of linseed oil, when external conditions such as mechanical stress or energy cause microcapsules to break. These controlled release mechanisms of linseed oil make them suitable for application in self-healing coatings. Chemical structure analyses of microcapsules were studied by Fourier transform infrared spectroscopy (FTIR), optical microscopy and scanning electron microscopy for their structural & morphological illustrations. Controllable particle sizes were determined under optical microscope and as well using particle size analyzer. To determine the healing efficiency, the microcapsules, were incorporated in the epoxy coatings in varying proportions. The effects of the same on anti-corrosion performance was carried out in 5% NaCl aqueous solution (ASTM B117) and Decreasing trend of pencil hardness, scratch hardness, Impact resistance with the increase in concentration of microcapsules was observed. Chemical resistance could also be attributed to the presence of aromatic structures in epoxy which impart chemical stability. Secondary hydroxyl moiety in epoxy chain forms hydrogen bonding with the metal substrate that would contribute to good adhesive forces. Epoxy coatings incorporated with microcapsules showed better corrosion resistance than neat epoxy coating, where neat epoxy coating showed rust and spreading of rust observed on tested panel. Mechanical properties decreased on incorporating microcapsules into epoxy matrix, hence development of mechanical properties without effecting the corrosion properties shall be studied further.