Amrik Singh; Devendra Mohan; Dharmavir S. Ahlawat; Sandeep Chopra
Volume 8, Issue 4 , April 2017, , Pages 565-571
Abstract
Indium Tin Oxide (ITO) coated glass acts as a substrate for photoanode of Dye Sensitized Solar Cells (DSSCs). The ITO substrate was irradiated by oxygen ion with different fluence (1x10 11 and 1x10 12 ions/cm 2 ) at 100 MeV energy. The TiO2 films were also subjected with same ion irradiation at 100 MeV ...
Read More
Indium Tin Oxide (ITO) coated glass acts as a substrate for photoanode of Dye Sensitized Solar Cells (DSSCs). The ITO substrate was irradiated by oxygen ion with different fluence (1x10 11 and 1x10 12 ions/cm 2 ) at 100 MeV energy. The TiO2 films were also subjected with same ion irradiation at 100 MeV of energy with fluence of 1x10 11 ions/cm 2 and 5x10 12 ions/cm 2 . At 100 MeV energy of O 7+ ion the electronic and nuclear energy loss for TiO2 film have been measured 7.38x10 -1 KeV/nm and 3.8x10 -4 KeV/nm respectively. However, the electronic and nuclear energy loss of ion irradiation for ITO substrate were 7.4x10 -1 KeV/nm and 4.06x10 -4 KeV/nm respectively. Similarly longitudinal/ lateral straggling of ITO and TiO2 have been found 3.87 μm/2.50 µm and 3.62 µm/1.14 μm respectively. Further, the structural and optical properties of these samples were monitored by X-ray diffraction (XRD), scanning electron microscopy (SEM) and UV-visible spectroscopy. It was found that oxygen ion (O 7+ ) irradiation of ITO film has slightly changed the crystallinity and transmission decreases. Furthermore, the particle size of TiO2 thin film has been obtained 80 nm corresponding to (101) plane of XRD pattern. In the case of ITO thin film the crystallite size and band gap changes from 62.35 nm to 53.89 nm and 3.993 eV to 3.971 eV at 1x10 12 ions/cm 2 respectively. Moreover this paper is also reporting that irradiation by swift heavy ion has changed the transmission of the ITO films, and its values decreases as compared to pristine (ITO) which degraded the performance of DSSC. Consequently, a very small value of absorbance is reported for ITO film. However, the absorbance of TiO2 film has found to increase with irradiation of oxygen ion at fluence of 1x10 12 ions/cm 2 and decreased at 5x10 12 ions/cm 2 . It is also confirmed that the absorbance of TiO2 film and TiO2/ITO photoanode increases with irradiation of oxygen ion at fluence of 1x10 12 ions/cm 2 and decreased at 5x10 12 ions/cm 2 . The band gap values of TiO2 thin film were obtained to have a change from 3.37 eV (for pristine) to 3.44 eV at 5x10 12 ions/cm 2 . But the decrease in band gap is also found 3.17 eV at fluence of 1x10 12 ions/cm 2 . However, N719 dye loaded O 7+ (1x10 12 ions/cm 2 ) irradiated TiO2 film show high absorption as compared to other samples. Thus the dose of O 7+ irradiation at fluence 1x10 12 ions/cm 2 may fabricate more efficient DSSC and consequently future prospective of such type of photoanode materials for dye sensitized solar cells seems to be bright.
Chaitanya Bathina; Krishnaiah Mokurala; Prasanth Ravindran; Parag Bhargava; Sudhanshu Mallick
Volume 7, Issue 11 , November 2016, , Pages 861-865
Abstract
Use of Pt and fluorine-doped tin oxide (FTO) substrate together as a counter electrode (CE) significantly increases the fabrication cost of dye-sensitized solar cells (DSSCs). In the present study, we report the cost effective Pt and FTO-free (Cu2ZnSnS4 (CZTS) nanoparticle coated on W substrate) CE for ...
Read More
Use of Pt and fluorine-doped tin oxide (FTO) substrate together as a counter electrode (CE) significantly increases the fabrication cost of dye-sensitized solar cells (DSSCs). In the present study, we report the cost effective Pt and FTO-free (Cu2ZnSnS4 (CZTS) nanoparticle coated on W substrate) CE for ZnO-based DSSCs. Phase purity, the morphology and elemental composition of synthesized ZnO, CZTS nanoparticles and films were confirmed by physical characteristics such as XRD, FEG-TEM, and FEG-SEM respectively. Cyclic voltammetry study confirmed electrochemical catalytic activity of CZTS films. DSSCs fabricated with CZTS film on W and FTO substrate as CE exhibited efficiencies of 2% and 2.8%, respectively. Conventionally used Pt-based CE demonstrated an efficiency of 3.8 %.