Baljinder Kaur; Lakhbir Singh; V. Annapu Reddy; Dae-Yong Jeong; Navneet Dabra; Jasbir S. Hundal
Abstract
Pure and Sr?doped bismuth ferrite Bi1-xSrx FeO3 (x = 0, 0.1, 0.2, 0.3) nanoparticles have been synthesized using combustion method. X- Ray diffraction study of these compounds confirms the rhombohedral structure with R3c space group. BiFeO3 peaks were observed at 2θ = 22.46o, 31.80o, 32.11o, 39.519o, ...
Read More
Pure and Sr?doped bismuth ferrite Bi1-xSrx FeO3 (x = 0, 0.1, 0.2, 0.3) nanoparticles have been synthesized using combustion method. X- Ray diffraction study of these compounds confirms the rhombohedral structure with R3c space group. BiFeO3 peaks were observed at 2θ = 22.46o, 31.80o, 32.11o, 39.519o, 45.79o, 51.35o, 56.98o and 57.16o having miller indices as (012), (104), (110), (202), (024), (116), (214) respectively. The traces of secondary phase also appear along with desired phase of Sr?doped bismuth ferrite Bi1-xSrxFeO3 samples. The scanning electron microscopy of fractured pellets of the samples reveals the decrease in grain size with increase of Sr doping in Bi1-xSrxFeO3. Magnetic studies were carried out at room temperature up to a field of 10 kOe. M-H hysteresis loops showed a significant increase in magnetization with Sr substitution in BiFeO3. Compared to weak magnetisation with magnetizing field (M-H) shown by BiFeO3 nanoparticles (Remnant magnetization, Mr ~ 0.4x10-3 emu/g and coercive field, Hc ~ 0.065 kOe respectively), a significant enhancement in M-H loop was observed in Bi1-xSrx FeO3 compounds. The value of Mr ~ 0.525 emu/g and Hc ~ 3.70 kOe have been found to be maximum for x = 0.30 in Bi1-xSrx FeO3 compounds. Leakage current studies showed decrease in leakage current density of doped samples to that of pure BiFeO3 and x = 0.10 gives minimum value of 4.78 x 10-6 A/cm2 at 350 V/cm. The ferroelectric nature was confirmed by observed P-E loops in all the samples.
Nikita H. Patel; M.P. Deshpande; Sandip V. Bhatt; Kamakshi R. Patel; S. H. Chaki
Abstract
Undoped and Mn doped CdS nanoparticles with varying Mn concentration of 10,15 and 20 mol % have been prepared by chemical co-precipitation method with polyvinylpyrrolidone (PVP) as capping agent at room temperature. EDAX has shown that no foreign impurities are present in the synthesized nanoparticles ...
Read More
Undoped and Mn doped CdS nanoparticles with varying Mn concentration of 10,15 and 20 mol % have been prepared by chemical co-precipitation method with polyvinylpyrrolidone (PVP) as capping agent at room temperature. EDAX has shown that no foreign impurities are present in the synthesized nanoparticles and X-ray diffraction (XRD) revealed that undoped and Mn doped CdS nanoparticles possess cubic phase with crystallite size ranging from 4-6 nm. Transmission electron microscopy (TEM) images indicated that nanoparticle sizes are between 2-6 nm and exhibits polycrystalline nature as seen from selected area electron diffraction (SAED) pattern. Raman spectra of undoped and Mn-doped CdS nanoparticles have shown 1LO and 2LO phonon modes and their intensity ratio decreases as Mn concentration increases. Magnetic susceptibility clearly pointed out that undoped CdS behaves as diamagnetic whereas Mn doped CdS as paramagnetic and varies nonlinearly with Mn concentration in CdS. Rapid increase in magnetization below 50 K temperature is observed in M-T curves which can be assigned to Mn ions isolated in CdS crystal field or extrinsic defects. The M-H curve at 5 K and 300 K for 20% Mn doped CdS nanoparticles at different magnetic fields showed no hystersis. In near future Mn doped CdS nanoparticles can be used for application in dilute magnetic semiconductor and fabrication of solar cells. The result and discussion drawn from this work are elaborated in detail in the paper.
Subhash B. Kondawar; Arti I. Nandapure; Bharti I. Nandapure
Abstract
Nanocrystalline nickel ferrite (NiFe2O4) powder of crystallite size ~20 nm was synthesized by refluxing method. Electrically conductive polyaniline-nickel ferrite (PANI/NiFe2O4) nanocomposites have been synthesized by an in-situ polymerization of aniline monomer in the presence of as-prepared NiFe2O4 ...
Read More
Nanocrystalline nickel ferrite (NiFe2O4) powder of crystallite size ~20 nm was synthesized by refluxing method. Electrically conductive polyaniline-nickel ferrite (PANI/NiFe2O4) nanocomposites have been synthesized by an in-situ polymerization of aniline monomer in the presence of as-prepared NiFe2O4 in different weight percentage (5%, 10%, and 15%). These nanocomposites were subsequently characterized for morphological, crystalline, structural, electrical and magnetic properties by Transmission Electron Microscopy (TEM), X-Ray Diffraction (XRD), Fourier Transform Infrared spectroscopy (FTIR), Four Probe Resistivity (FPR) and Vibrating Sample Magnetometer (VSM). Existence of NiFe2O4 in the nanocomposites was confirmed by XRD, FTIR and TEM analysis. The change in morphology with crystallite size ? 50 nm was observed for the nanocomposites clearly indicate the coating of PANI on NiFe2O4 . Nanocomposites showed increase in saturation magnetization as compared to that of PANI and increase in electrical conductivity as compared to that of NiFe2O4 indicating the synergistic effect of individual components. The saturation magnetization drastically increased as nickel ferrite content changed from 5 to 15% in nanocomposites. The conductivity of nanocomposites increased with temperature, exhibiting typical semiconductor behavior. The nanocomposites show semiconducting and ferromagnetic behaviour. The electrical conductivity of nanocomposites decreased from 1.089 to 0.268 S/cm, but saturation magnetization increased from 0.97 to 2.803 emu/g, when ferrite content changed from 5 to 15 wt%, indicates such nanocomposites are good for electromagnetic devices.
Abstract
Nickel oxide (NiO) nanoparticles were prepared by the simple approach of co-precipitation method using nickel carbonate as precursor. Novel electrically conducting composite materials consisting of nickel oxide nanoparticles dispersed in a polyaniline (PANI) are prepared by an in-situ polymerization ...
Read More
Nickel oxide (NiO) nanoparticles were prepared by the simple approach of co-precipitation method using nickel carbonate as precursor. Novel electrically conducting composite materials consisting of nickel oxide nanoparticles dispersed in a polyaniline (PANI) are prepared by an in-situ polymerization method in the presence of different weight percentage of NiO (5, 10, 15 and 20%) at room temperature using ammonium persulphate (NH4)2S2O8 as an oxidant in acidic medium. The synthesized PANI/NiO nanocomposites have been characterized by means of XRD, FTIR, UV-VIS, TEM and VSM for structural and magnetic investigation. NiO has single phase cubic structure with average crystallite size of 23nm and is intercalated to form a core shell of PANI due to which nanocomposites show the peaks of NiO as well as PANI. PANI/NiO nanocomposites showed semiconducting as well as ferromagnetic nature. It was also observed that the conductivity of the PANI/NiO nanocomposites decreased and the magnetization increased with the increase in weight percentage of NiO in PANI. We studied first time the effect of NiO on transport properties of PANI/NiO nanocomposites in terms of transport parameters such as electrical conductivity (s), charge localization length (a-1), most probable hopping distance (R) and charge hopping energy (w) using variable range hoping (VRH) of charge model as described by Ziller to conducting polymers.Copyright © 2013 VBRI press.
Samar Layek; Soumen Kumar Bag;H.C. Verma
Abstract
Multiferroic nano-composite (1-x) BiFeO3–x Li0.5Fe2.5O4 (x=0.25 and 0.5) have been successfully synthesized by mixing the two phases, prepared independently by two different methods followed by annealing at 600 0C. Existence of the two phases in the composite is confirmed by x-ray diffraction pattern. ...
Read More
Multiferroic nano-composite (1-x) BiFeO3–x Li0.5Fe2.5O4 (x=0.25 and 0.5) have been successfully synthesized by mixing the two phases, prepared independently by two different methods followed by annealing at 600 0C. Existence of the two phases in the composite is confirmed by x-ray diffraction pattern. Average particle size is calculated to be about 45 nm for both of these phases. The saturation magnetization, remnant magnetization and coercive field increases linearly with increasing ferromagnetic phase (Li0.5Fe2.5O4) as investigated by VSM measurement. Local magnetic behaviors have been investigated by 57Fe Mössbauer spectroscopic studies. Large dielectric constant of the order of 10 3 -10 4 has been observed in these composites.
Samar Layek;H.C. Verma
Abstract
Single phase BiFeO3 nanoparticles have been successfully synthesized for the first time by a novel citrate combustion method without using any solvent. Well mixed metal nitrates along with citric acid which is used as fuel combust to give BiFeO3 nanoparticles after annealing. These particles are ...
Read More
Single phase BiFeO3 nanoparticles have been successfully synthesized for the first time by a novel citrate combustion method without using any solvent. Well mixed metal nitrates along with citric acid which is used as fuel combust to give BiFeO3 nanoparticles after annealing. These particles are single phase in nature and crystallize in the rhombohedral distorted perovskite structure (space group-R3c) which has been confirmed by the Rietveld refinement of the room temperature powder x-ray diffraction data. Nearly spherical particles of average particle size 47 nm have been seen from transmission electron micrograph. Room temperature magnetic hysteresis measurement shows weak ferromagnetism though the magnetization does not saturate upto 1.75 T applied field. The coercive field value is calculated to be 180 Oe which is 3 times higher than that prepared by solvent free combustion method using glycine. 57 Fe Mössbauer spectrum can be fitted with a sextet corresponding to single magnetic state of hyperfine field about 49.5 T corresponding to Fe 3+ state of the iron atom. The dielectric relaxation and ac conductivity as a function of frequency have been discussed. High dielectric permittivity has not been found in these nanoparticles like other reported BiFeO3 ceramics.
Gagan Dixit; J.P. Singh; R.C. Srivastava; H.M. Agrawal; R.J. Chaudhary
Abstract
In the present work, structural, morphological, magnetic and optical properties of nickel ferrite thin films having different thickness are reported. All the films were deposited on Si (100) substrate by pulsed laser deposition technique. Thicknesses of the films determined by x-ray reflectivity vary ...
Read More
In the present work, structural, morphological, magnetic and optical properties of nickel ferrite thin films having different thickness are reported. All the films were deposited on Si (100) substrate by pulsed laser deposition technique. Thicknesses of the films determined by x-ray reflectivity vary from 62 to 176nm as the deposition time varies from 16 min to 40 min. The films were characterised by x-ray diffractogram, Fourier transform infrared (FTIR) and Raman spectroscopy for structural and phase confirmation. FTIR and Raman spectra confirm mixed spinel nature of nickel ferrite. Surface morphology is studied by Atomic force microscopy. All the films have granular nature. Magnetic properties were studied by vibrating sample magnetometer and magnetic hysteresis curves were recorded for all the films at room temperature and at10K. At 10K, saturation magnetisation was found to increase while coercivity deceases with thickness. The results are explained on the basis of anisotropy induced by cation inversion and strain. Optical properties were studied by UV-vis reflectance spectra. The value of optical band gap (5.7eV) was found to be independent of thickness of the film.