Balakrishnan G; Elangovan T; Shin-Sung Yoo; Dae-Eun- Kim; Kuppusami P; Venkatesh Babu R; Sastikumar D; Jung il Song
Abstract
Nanostructured single layer aluminium oxide (Al2O3), single layer zirconium oxide (ZrO2) and the (Al2O3/ZrO2) nano multilayer films were deposited on Si (100) substrates at an optimized oxygen pressure of 3×10 -2 mbar at room temperature by pulsed laser deposition. The Al2O3 layer was kept constant ...
Read More
Nanostructured single layer aluminium oxide (Al2O3), single layer zirconium oxide (ZrO2) and the (Al2O3/ZrO2) nano multilayer films were deposited on Si (100) substrates at an optimized oxygen pressure of 3×10 -2 mbar at room temperature by pulsed laser deposition. The Al2O3 layer was kept constant at 5 nm, while ZrO2 layer thickness was varied from 5 nm to 20 nm. The X-ray diffraction (XRD) studies of single layer of Al2O3 film indicated the cubic γ-Al2O3, while the single layer of ZrO2 indicated both the monoclinic and tetragonal phases. The Al2O3/ZrO2 multilayer films of 5/5 nm and 5/10 nm indicated the tetragonal phase of ZrO2 with nanocrystalline nature. The FESEM and AFM studies showed the dense and smooth morphology of the films. The pin-on disc revealed that the 5/10 nm multilayer film has low friction coefficient ~ 0.10. The wear rate of multilayers film is half of the wear rate of the single layer films and 5/10 nm multilayer film showed a reduced wear rate when it is compared to other single and multilayers. The Al2O3-ZrO2 ceramics find wide applications in wear and corrosion resistance components, high temperature applications and bio-implant materials.